不同直径纤维混合玻璃纤维纸的保温隔音性能

发布时间:2019-01-04 21:33  文章来源:笔耕文化传播
【摘要】:玻璃纤维纸是一种优良的阻燃保温隔音过滤材料,在高铁、航空航天和航海领域有广泛的应用。本文通过湿法打浆工艺制备不同纤维混合的玻璃纤维纸,重点探究其孔径分布、透气性能、保温性能以及隔音性能。结果表明:随着玻璃纤维纸中细纤维含量的增加,平均孔径和透气率先减小后增加;随着玻璃纤维纸中细纤维含量的增加,纸张的导热系数先降低后升高,隔音量先升高后降低。纤维配比为粗纤维50%+细纤维50%,玻璃纤维纸的保温隔音性能最佳。
[Abstract]:Glass fiber paper is a kind of excellent flame retardant, insulation and sound filter material, which has been widely used in the fields of high-speed, aerospace and navigation. In this paper, glass fiber paper with different fibers was prepared by wet beating process, and its pore size distribution, air permeability, heat preservation and sound insulation were investigated. The results show that the average pore size and air permeability decrease first and then increase with the increase of the content of fine fiber in glass fiber paper. With the increase of the content of fine fiber in glass fiber paper, the thermal conductivity of paper first decreases and then increases, and the sound insulation content increases first and then decreases. Fiber ratio is 50% coarse fiber fine fiber 50, glass fiber paper insulation sound insulation performance is the best.
【作者单位】: 南京航空航天大学绝热与节能材料国际实验室;
【基金】:江苏省联合载体项目(BM2016010)资助项目
【分类号】:TQ171.777.73

【相似文献】

相关期刊论文 前10条

1 ;玻璃纤维纸试制成功并进行了鉴定[J];玻璃纤维;1972年02期

2 格奥;;多种用途的玻璃纤维纸[J];玻璃纤维;1980年05期

3 西松三郎;钱世准;;玻璃纤维纸[J];玻璃纤维;1980年03期

4 王鹏;如何提高玻璃纤维纸的玻纤分散性[J];纸和造纸;2002年06期

5 ;“G—1”超细玻璃纤维纸[J];玻璃纤维;1977年01期

6 孙立霞;湿法玻璃纤维纸的制造技术及其用途[J];江苏建材;1997年03期

7 叶鼎铨;;挤压法拉丝即将投入工业化生产[J];玻璃纤维;1978年05期

8 亦云;;日本玻璃纤维无纺织物的发展动向[J];玻璃纤维;1990年05期

9 辜信实,罗宜才;覆铜板用E玻璃纤维纸[J];绝缘材料通讯;2000年02期

10 顾勇华;;用玻璃纸代替石棉垫片[J];玻璃纤维;1980年06期



本文编号:2400820


论文下载
论文发表
教材专著
专利申请


    下载步骤:1.微信扫码 2.备注编号 2400820. 3.下载文档
    注:1.必须备注编号,否则无法下载;2.扫码后10分钟即可下载,如有问题,点击微信联系客服。


    本文链接:http://www.bigengculture.com/kejilunwen/huagong/2400820.html

    上一篇:EDTA返滴定法测定铅玻璃中铅  
    下一篇:没有了